Vật liệu hàn hồ quang chìm

Superflux600 x A-3

Superflux 600 Superflux600 x A-3

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-M5
EN ISO 14174 S A AB 1 / 14171 S4Mo
KS
AWS A5.23/ASME SFA5.23 F8A(P)4-EA3-G
  • Caution ① Dry the flux at 300~350℃ (572~662°F ) for 60 minutes before use.

    ② In case of multi-layer welding of the thick plate, to prevent cracks, low current and low speed welding should be performed on the lower layer.

    ③ If weld heat input is managed below 31KJ/cm, a better impact toughness can be achieved.

    ④ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Structure fabrication (HSB500(SM490) and HSB600(SM570))
  • Attribute ① Good bead appearance

    ② Easy to remove slag

    ③ Good resistance to pockmarks and pits

    ④ Density : 1.2g/cm3

Superflux600 x H-14

Superflux 600 Superflux600 x H-14

Type
Industry
JIS Z3352 S A AB 1 / Z3351 YS-S6
EN ISO 14174 S A AB 1 / 14171 S4
KS
AWS A5.17/ASME SFA5.17 F7A(P)6-EH14
  • Caution ① Dry the flux at 300~350℃ (572~662°F ) for 60 minutes before use.

    ② In case of multi-layer welding of the thick plate, to prevent cracks, low current and low speed welding should be performed on the lower layer.

    ③ If weld heat input is managed below 31KJ/cm, a better impact toughness can be achieved.

    ④ When restraint stress is high or welding a thick plate, preheat according to rules.
  • Purpose ① Structure fabrication (HSB500(SM490) and HSB600(SM570))
  • Attribute ① Good bead appearance

    ② Easy to remove slag

    ③ Good resistance to pockmarks and pits

    ④ Density : 1.2g/cm3