Industry
JIS Z3252 DFCFe
EN ISO 1071 - E Z 1
KS D7008 DGCFe
AWS A5.15/ASME SFA5.15 ESt
  • Caution ① The preheat temperatures vary in accordance with the size, kind and shape of the base metal. 150℃(302℉) is appropriate in general.

    ② Gradual cooling recommended after welding

    ③ Keep the weld metal length less than 50mm(2 inch) to disperse welding heat. Adopt back stepping stone or symmetry method by turns.
  • Purpose ① Repairing of cast iron
  • Attribute ① Machining impossible (As welded)

    ② Easy to remove slag

    ③ Preheat at 200~350°C (392~662°F)

    ④ Stable arc and good bead appearance

S-NFC

Gang S-NFC

Type
Industry
JIS Z3252 DFCNiFe
EN ISO 1071 - E C NiFe-CI 1
KS D7008 DGCNiFe
AWS A5.15/ASME SFA5.15 ENiFe-CI
  • Caution ① Use currents as low as possible.

    ② Keep the weld metal length less than 50mm(2 inch) to disperse welding heat.

    ③ The preheat temperatures vary in accordance with the size, kind and shape of the base metal. 100~200℃(212~392℉) is appropriate in general.
  • Purpose ① Welding of normal grades of cast iron
  • Attribute ① Good crack resistance

    ② Preheat at 100~200°C (212~392°F)

    ③ Easy to remove slag

S-NCI

Gang S-NCI

Type Basic
Industry
JIS Z3252 DFCNi
EN ISO 1071 - E C Ni-CI 1
KS D7008 DGCNi
AWS A5.15/ASME SFA5.15 ENi-Cl
  • Caution ① Chip off base metal completely at the repairing part.

    ② There is a possibility that cracks spreads or makes holes at both ends of repairing part.

    ③ Keep the weld metal length less than 50mm(2 inch) to disperse welding heat. Adopt back stepping stone or symmetry method by turns.

    ④ The preheat temperatures vary in accordance with the size, kind and shape of the base metal. 150℃(302℉) is appropriate in general.
  • Purpose ① Repairing and joining of cast iron
  • Attribute ① Graphite coated electrode

    ② Preheat at 150°C (302°F)