Fülldrahtelektroden

SW-410 Cored

Nichtrostende Stähle SW-410 Cored

Type Rutile
Industry Martensite stainless steel welding
JIS Z3323 TS410-FB1
EN
KS D6312 YF410LC
AWS A5.22 E410T1-1/-4
  • Caution .
  • Purpose ① 410, 410S, 405 stainless steels

    ② Welding of ASTM CA6NM castings
  • Attribute ① Weld metal of martensite stainless steel

    ② Good hardness and anti-abrasion properties

SC-439TiCored

Nichtrostende Stähle SC-439TiCored

Type Metal-Cored
Industry Automotive
JIS
EN
KS
AWS A5.22 EC439
  • Caution ① Keep preheating and interpass temperature to be more than 150℃(302℉).

    ② PWHT at 850℃(1,562°F) will improve mechanical properties and corrosion resistance.

    ③ As there is higher chance of cracks for this grade, extra care is needed when welding. ④ Use Ar or Ar + 2-5% O₂ mixed gas.
  • Purpose ① Stainless steels 409, 430, 436, 439 Type • Automotive mufflers
  • Attribute ① Good corrosion resistance

    ② Low spatter

    ③ Non-slag type

SF-436

Nichtrostende Stähle SF-436

Type Metal-Cored
Industry Automotive
JIS
EN
KS
AWS
  • Caution ① Keep preheating and interpass temperature to be more than 150℃(302℉).

    ② PWHT at 850℃(1,562°F) will improve mechanical properties and corrosion resistance.

    ③ As there is higher chance of cracks for this grade, extra care is needed when welding.

    ④ Use Ar or Ar + 2-5% O₂ mixed gas."
  • Purpose ① Stainless steels 409, 430 and 436 Type

    ② Automotive mufflers
  • Attribute ① Good corrosion resistance

    ② Low spatter

    ③ Non-slag type

SF-430Nb

Nichtrostende Stähle SF-430Nb

Type Metal-Cored
Industry Automotive
JIS Z3323 TS430Nb-MAO
EN
KS
AWS
  • Caution ① Use Ar or Ar + 2-5% O₂ mixed gas.
  • Purpose ① Stainless steels 409 and 430 Type

    ② Automotive mufflers
  • Attribute ① Good corrosion resistance

    ② Low spatter

    ③ Non-slag type

SF-430

Nichtrostende Stähle SF-430

Type Metal-Cored
Industry Automotive
JIS Z3323 TS430-MAO
EN
KS
AWS A5.9 EC430
  • Caution ① Keep preheating and interpass temperature to be more than 150℃(302℉).

    ② PWHT at 850℃(1,562°F) will improve mechanical properties and corrosion resistance.

    ③ As there is higher chance of cracks for this grade, extra care is needed when welding.

    ④ Use Ar or Ar + 2-5% O₂ mixed gas.
  • Purpose ① Stainless steels 409 and 430 Type

    ② Automotive mufflers
  • Attribute ① Good corrosion resistance

    ② Low spatter

    ③ Non-slag type

SF-409Ti

Nichtrostende Stähle SF-409Ti

Type Metal-Cored
Industry Automotive
JIS Z3323 TS409-MAO
EN
KS
AWS A5.9 EC409
  • Caution ①Use Ar or Ar + 2-5% O₂ mixed gas.
  • Purpose ① Stainless steels 409 Type

    ② Automotive mufflers
  • Attribute ① Good corrosion resistance

    ② Low spatter

    ③ Non-slag type

Supercored 316L

Nichtrostende Stähle Supercored 316L

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS316L-FB0
EN ISO 17633-A-T 19 12 3 L R M21/C1 3
KS D3612 YF316LC
AWS A5.22 E316LTO-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 18%Cr-12%Ni-2%Mo stainless steels
  • Attribute ① Flat and horizontal fillet position welding

    ② High deposition rate and efficiency

Supercored 309MoL

Nichtrostende Stähle Supercored 309MoL

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS309LMo-FB0
EN ISO 17633-A-T 23 12 2 L R M21/C1 3
KS D3612 YF309LMoC
AWS A5.22 E309LMoTO-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 22%Cr-12%Ni-2.5%Mo stainless steels

    ② Dissimilar welds between carbon, low alloy steels to stainless steels

    ③ Buffer layer welding for cladding, overlays
  • Attribute ① Flat and horizontal fillet position welding

    ② High deposition rate and efficiency

Supercored 309L

Nichtrostende Stähle Supercored 309L

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS309L-FB0
EN ISO 17633-A-T 23 12 L R M21/C1 3
KS D3612 YF309LC
AWS A5.22 E309LTO-1-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 23.5%Cr-13%Ni stainless steels

    ② Dissimilar welds between carbon, low alloy steels to stainless steels

    ③ Buffer layer welding for cladding, overlays
  • Attribute ① Flat and horizontal fillet position welding

    ② High deposition rate and efficiency

Supercored 308L

Nichtrostende Stähle Supercored 308L

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS308L-FB0
EN ISO 17633-A-T 19 9 L R M21/C1 3
KS D3612 YF308LC
AWS A5.22 E308LTO-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 18%Cr-8%Ni stainless steel
  • Attribute ① Flat and horizontal fillet position welding

    ② High deposition rate and efficiency

SW-2209 Cored

Nichtrostende Stähle SW-2209 Cored

Type Rutile
Industry Duplex stainless steel welding
JIS Z3323 TS2209-FB1
EN ISO 17633-A-T 22 9 3 N L M21/C1 2
KS
AWS A5.22 E2209T1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① Duplex stainless steel (NAS 329J3L, UNS S31803)
  • Attribute ① Good performance in all positions

SW-410NiMo Cored

Nichtrostende Stähle SW-410NiMo Cored

Type Rutile
Industry Martensite stainless steel welding
JIS Z3323 TS410NiMo-FB1
EN ISO 17633-A-T 13 4 P M21/C1 2
KS
AWS A5.22/ E410NiMoT1-1/-4
  • Caution ① Preheat the base metal for more than 150℃(302℉).

    ② Use 100% CO₂ gas or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① Martensite stainless steels (ASTM, CA6NM)

    ② Hardfacing of continuos casting rolls, valve seat, etc

    ③ Power plant
  • Attribute ① Good performance in all positions

SW-347 Cored

Nichtrostende Stähle SW-347 Cored

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS347-FB1
EN ISO 17633-A-T 19 9 Nb P M21/C1 2
KS D3612 YF347C
AWS A5.22 E347T1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① Stainless steel boilers and gas turbine

    ② 347 and 321 type stainless steels
  • Attribute ① Good performance in all positions

SW-317L Cored

Nichtrostende Stähle SW-317L Cored

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS317L-FB1
EN ISO 17633-A-T 19 13 4 P M21/C1 2
KS D3612 YF317LC
AWS A5.22 E317LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 316, 317 type stainless steels
  • Attribute ① Good performance in all positions

SW-316LT

Nichtrostende Stähle SW-316LT

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS316L-FB1
EN
KS
AWS A5.22 E316LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.

    ② Storage in high temperature and humid place for a long time might cause welding defects caused by moisture absortion.

    ③ Windshield would be required when welding in a windy place.

    ④ Lowering the voltage for 2 volts is recommended when using mixed gas, compared to when using 100% CO2 gas.
  • Purpose ① Cryogenic service such as LNG storage tank

    ② 18% Cr-12%Ni-2%Mo stainless steels
  • Attribute ① Good impact value at cryogenic temperature ② Good performance in all position

SW-316L Cored

Nichtrostende Stähle SW-316L Cored

Type Rutile
Industry Shipbuilding
JIS Z3323 TS316L-FB1
EN ISO 17633-A-T 19 12 3 L P M21/C1 2
KS D3612 YF316LC
AWS A5.22 E316LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 18%Cr-12%Ni-2%Mo stainless steels
  • Attribute ① Good performance in all positions

SW-309MoL Cored

Nichtrostende Stähle SW-309MoL Cored

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS309LMo-FB1
EN ISO 17633-A-T 23 12 2 L P M21/C1 2
KS D3612 YF309LMoC
AWS A5.22 E309LMoT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 22%Cr-12%Ni-2.5%Mo stainless steels

    ② Dissimilar welds between carbon, low alloy steels to stainless steels

    ③ Buffer layer welding for cladding, overlays
  • Attribute ① Good performance in all positions

SW-309LNS Cored

Nichtrostende Stähle SW-309LNS Cored

Type Metal-Cored
Industry Automotive
JIS Z3323 TS309L-MA0
EN ISO 17633-A-T 23 12 L M M21/I1
KS
AWS A5.9 EC309L
  • Caution ① Use Ar or Ar + 2-5% O₂ mixed gas.
  • Purpose ① Automotive mufflers

    ② Welding of dissimilar metals such as stainless and carbon a low alloy steels
  • Attribute ① Non-slag type

    ② Low spatter

SW-309L Cored

Nichtrostende Stähle SW-309L Cored

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS309L-FB1
EN ISO 17633-A-T 23 12 L P M21/C1 2
KS D3612 YF309LC
AWS A5.22 E309LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 23.5%Cr-13%Ni stainless steels

    ② Dissimilar welds between carbon, low alloy steels to stainless steels

    ③ Buffer layer welding for cladding, overlays
  • Attribute ① Good performance in all positions

SW-308LT

Nichtrostende Stähle SW-308LT

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS308L-FB1
EN ISO 17633-A-T 19 9 L P M21/C1 2
KS D3612 YF308LC
AWS A5.22 E308LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.

    ② Storage in high temperature and humid place for a long time might cause welding defects caused by moisture absortion.

    ③ Windshield would be required when welding in a windy place.

    ④ Lowering the voltage for 2 volts is recommended when using mixed gas, compared to when using 100% CO2 gas.
  • Purpose ① Cryogenic service such as LNG storage tank

    ② 18% Cr-8%Ni stainless steels
  • Attribute ① Good impact value at cryogenic temperatures

    ② Good performance in all positions

SW-308L Cored

Nichtrostende Stähle SW-308L Cored

Type Rutile
Industry Austenite stainless steel welding
JIS Z3323 TS308L-FB1
EN ISO 17633-A-T 19 9 L P M21/C1 2
KS D3612 YF308LC
AWS A5.22 E308LT1-1/-4
  • Caution ① Use 100% CO₂ or Ar + 20-25% CO₂ mixed gas.
  • Purpose ① 18%Cr-8%Ni stainless steel
  • Attribute ① Good porosity resistance

    ② Good performance in all positions

SW-307NS Cored

Nichtrostende Stähle SW-307NS Cored

Type Metal
Industry Austenite stainless steel welding
JIS
EN ISO 17633-A-T 18 8 Mn M M
KS
AWS
  • Caution ① Use Ar or Ar + 2-5% O₂ mixed gas.

    ② Storage in high temperature and humid place for a long time might cause welding defects caused by moisture absortion.

    ③ Windshield would be required when welding in a windy place.
  • Purpose ① Joining and overlay applications on 13Mn steels

    ② Cladding Carbon steels

    ③ Welding of dissimilar steels (high Mn to carbon steel)
  • Attribute ① Flat and horizontal fillet position welding

    ② High deposition rate and efficiency