Superflux300S x YS-316(L)

Superflux 300S Superflux300S x YS-316(L)

Type
Industry
JIS Z3324 FSS-B1/YS316(L)
EN
KS
AWS
  • Caution ① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.

    ② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.

    ③ Welding in groove should be done in 2 passes to ease slag removal.
  • Purpose ① 18%Cr-8%Ni stainless steel
  • Attribute ① Good resistance to crack and corrosion

    ② Easy to remove slag

    ③ Good bead appearance

    ④ Density : 1.2g/cm3

Superflux300S x YS-309(L)

Superflux 300S Superflux300S x YS-309(L)

Type
Industry
JIS Z3324 FSS-B1/YS309(L)
EN
KS
AWS
  • Caution ① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.

    ② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.

    ③ Welding in groove should be done in 2 passes to ease slag removal."
  • Purpose ① 18%Cr-8%Ni stainless steel
  • Attribute ① Good resistance to crack and corrosion

    ② Easy to remove slag

    ③ Good bead appearance

    ④ Density : 1.2g/cm3

Superflux300S x YS-308(L)

Superflux 300S Superflux300S x YS-308(L)

Type
Industry
JIS Z3324 FSS-B1/YS308(L)
EN
KS
AWS
  • Caution ① Dry the flux at 300~350°C (572~662°F ) for 60 minutes before use.

    ② Avoid using high current to prevent harming of corrosion-resistibility in heat-affected zone, heat input in welding should be kept as low as possible.

    ③ Welding in groove should be done in 2 passes to ease slag removal.
  • Purpose ① 18%Cr-8%Ni stainless steel
  • Attribute ① Good resistance to crack and corrosion

    ② Easy to remove slag

    ③ Good bead appearance

    ④ Density : 1.2g/cm3