Électrodes

S-308L.15

Stainless Steel S-308L.15

Type
Industry
JIS
EN ISO 3581- A - E 19 9 L B
KS
AWS A5.4/ASME SFA5.4 E308L-15
  • Caution .
  • Purpose ① Stainless steel(18%Cr-8%)
  • Attribute ① Good resistance to corrosion and oxidizing environments

    ② Easy to remove slag

    ③ Low spatter

    ④ Good bead appearance

S-308H.16

Stainless Steel S-308H.16

Type Rutile
Industry
JIS Z3221 ES308H-16
EN ISO 3581- A - E 19 9 H R 3 2
KS
AWS A5.4/ASME SFA5.4 E308H-16
  • Caution .
  • Purpose ① Stainless steel (ASTM 304H, 304)
  • Attribute ① Good creep resistance

    ② Service temperature up to 700°C(1292°F)

    ③ Easy to remove slag

    ④ Low spatter

    ⑤ Good bead appearance

S-309L.17

Stainless Steel S-309L.17

Type
Industry
JIS Z3221 ES309L-17
EN ISO 3581- A - E 23 12 L R
KS
AWS A5.4/ASME SFA5.4 E309L-17
  • Caution .
  • Purpose ① Welding of dissimilar steels

    ② Buffer layer for bulid-up
  • Attribute ① Good resistance to heat and corrosion

    ② Good crack resistance

    ③ Easy to remove slag

    ④ High moisture resistance (17 type)

S-309L.15

Stainless Steel S-309L.15

Type Basic
Industry
JIS Z3221 ES309L-15
EN ISO 3581- A - E 23 12 L B
KS
AWS A5.4/ASME SFA5.4 E309L-15
  • Caution .
  • Purpose ① Welding of dissimilar steels

    ② Buffer layer for bulid-up
  • Attribute ① Good resistance to heat and corrosion

    ② Good crack resistance

    ③ Easy to remove slag

S-2209.16

Stainless Steel S-2209.16

Type Rutile
Industry
JIS Z3221 ES2209-16
EN ISO 3581- A - E 22 9 3 N L
KS
AWS A5.4/ASME SFA5.4 E2209-16
  • Caution ① Remove rust, water, oil and paint from the groove.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible and length as short as possible.
  • Purpose ① Welding of duplex stainless steel (SAF2205, UNS S31803)
  • Attribute ① Ferritic/austenitic structure (All-weld metal)

    ② Service temperature up to 250°C

    ③ High resistance to pitting, intergranular and stress corrosion

    ④ PREN 35

    ⑤ Easy to remove slag

    ⑥ Good bead appearance

S-347.16

Stainless Steel S-347.16

Type Rutile
Industry Energy & Power Plants|Pipe & Pipeline
JIS Z3221 ES347-16
EN ISO 3581- A - E 19 9 Nb R
KS D7014 E347-16
AWS A5.4/ASME SFA5.4 E347-16
  • Caution ① Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ② Remove rust, water, oil and paint from the surface to be welded.

    ③ Keep the arc as short as possible.
  • Purpose ① Stainless steel (321, 347)
  • Attribute ① Contains stabilizing element(Nb)

    ② High temperature strength

    ③ Suitable for welding of boiler and gas turbine

    ④ Easy to remove slag

S-317L.16

Stainless Steel S-317L.16

Type Rutile
Industry Shipbulding|Offshore Structures|Energy & Power Plants
JIS Z3221 ES317L-16
EN
KS D7014 E317L-16
AWS A5.4/ASME SFA5.4 E317L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Remove rust, water, oil and paint from the groove.
  • Purpose ① Stainless steel (317L)
  • Attribute ① Good resistance to nitroxide and sulfide

    ② Good heat resistance

    ③ Easy to remove slag

S-316LT.16

Stainless Steel S-316LT.16

Type Rutile
Industry Offshore structure
JIS Z3221 ES316L-16
EN ISO 3581- A - E 19 12 3 L R
KS D7014 E316L-16
AWS A5.4/ASME SFA5.4 E316L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible

    ④ Remove rust, water, oil and paint from the groove.
  • Purpose ① Stainless steel (18%Cr-12%Ni-2%Mo)

    ② LPG, LNG storage tank
  • Attribute ① Good impact value up to -196°C

    ② Good resistance to inter-crystalline corrosion ③ Easy to remove slag

    ③ Low spatter

S-316L.16N

Stainless Steel S-316L.16N

Type Rutile
Industry Shipbulding|Offshore Structures|Energy & Power Plants|Steel Fabricatio
JIS Z3221 ES316L-16
EN ISO 3581- A - E 19 12 3 L R
KS D7014 E316L-16
AWS A5.4/ASME SFA5.4 E316L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible

    ④ Remove rust, water, oil and paint from the groove.
  • Purpose ① Stainless steel (low carbon 18%Cr-12%Ni-2%Mo)
  • Attribute ① Good resistance to corrosion and oxidizing environments

    ② Good heat resistance

    ③ easy to remove slag

    ④ High moisture resistance (17 type)

S-316.16N

Stainless Steel S-316.16N

Type Rutile
Industry
JIS Z3221 ES316-16
EN ISO 3581- A - E 19 12 3 R
KS D7014 E316-16
AWS A5.4/ASME SFA5.4 E316-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Stainless steel (18%Cr-12%Ni-2%Mo)
  • Attribute ① Good resistance to corrosion and oxidizing environments

    ② Good heat resistance

    ③ easy to remove slag

    ④ Low spatter

S-312.16

Stainless Steel S-312.16

Type Rutile
Industry Energy & Power Plants|Steel Fabrication
JIS Z3221 ES312-16
EN ISO 3581- A - E 29 9 R
KS D7014 E312-16
AWS A5.4/ASME SFA5.4 E312-16
  • Caution ① Preheat the base metal at over 200℃(392℉) to prevent cracking in welding of high alloyed steel, having good harden ability such as tool steel.

    ② Keep the current as low as possible and length as short as possible.

    ③ Dry the electrodes at 350℃(662℉) for 60 minutes before use.
  • Purpose ① Welding of dissimilar steels

    ② Buffer layer for bulid-up
  • Attribute ① Good crack resistance

    ② Excellent buffer effect against stress

    ③ Easy to remove slag

S-310.16

Stainless Steel S-310.16

Type Rutile
Industry Energy & Power Plants|Steel Fabrication
JIS Z3221 ES310-16
EN ISO 3581- A - E 25 20 R
KS D7014 E310-16
AWS A5.4/ASME SFA5.4 E310-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Stainless steel (25%Cr-20%Ni)
  • Attribute ① Good heat resistance

    ② Good mechanical properties

    ③ Martensite structure (All-weld metal)

    ④ Easy to remove slag

S-310.15

Stainless Steel S-310.15

Type Low-hydrogen Type
Industry Energy & Power Plants|Steel Fabrication
JIS Z3221 ES310-15
EN ISO 3581- A - E 25 20 B
KS D7014 E310-15
AWS A5.4/ASME SFA5.4 E310-15
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Welding of 13%Cr or clad part of 18%Cr-8%Ni steel
  • Attribute ① Basic type electrode

    ② Good mechanical properties

    ③ Martensite structure (All-weld metal)

S-309MoL.16

Stainless Steel S-309MoL.16

Type Rutile
Industry Shipbulding|Offshore Structures|Energy & Power Plants|Steel Fabricatio
JIS Z3221 ES309LMo-16
EN ISO 3581- A - E 23 12 2 L R
KS D7014 E309MoL-16
AWS A5.4/ASME SFA5.4 E309LMo-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Welding of dissimilar steels

    ② Welding of low carbon 22%Cr-12%Ni-2.5%Mo stainless steel
  • Attribute ① Good resistance to heat and crack

    ② Easy to remove slag

    ③ Good bead appearance

S-309Mo.16

Stainless Steel S-309Mo.16

Type Rutile
Industry
JIS Z3221 ES309Mo-16
EN ISO 3581- A - E 23 12 2 R
KS D7014 E309Mo-16
AWS A5.4/ASME SFA5.4 E309Mo-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Welding of dissimilar steels

    ② Welding of low carbon 22%Cr-12%Ni-2.5%Mo stainless steel
  • Attribute ① Good resistance to heat and crack

    ② Easy to remove slag

    ③ Good bead appearance

S-309L.16

Stainless Steel S-309L.16

Type Rutile
Industry Shipbulding|Offshore Structures|Energy & Power Plants|Steel Fabricatio
JIS Z3221 ES309L-16
EN ISO 3581- A - E 23 12 L R
KS D7014 E309L-16
AWS A5.4/ASME SFA5.4 E309L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Welding of dissimilar steels

    ② Buffer layer for bulid-up
  • Attribute ① Good resistance to heat and corrosion

    ② Good crack resistance

    ③ Easy to remove slag

    ④ High moisture resistance (17 type)

S-309.16N

Stainless Steel S-309.16N

Type Rutile
Industry
JIS Z3221 ES309-16
EN ISO 3581- A - E 23 12 R
KS D7014 E309-16
AWS A5.4/ASME SFA5.4 E309-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the current as low as possible
  • Purpose ① Welding of dissimilar steels
  • Attribute ① Good resistance to heat and corrosion

    ② Easy to remove slag

    ③ Low spatter

S-308LT.16

Stainless Steel S-308LT.16

Type Rutile
Industry Steel Fabrication
JIS Z3221 ES308L-16
EN ISO 3581- A - E 19 9 L R
KS D7014 E308L-16
AWS A5.4/ASME SFA5.4 E308L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Remove dirts such as oil and dust from the groove.

    ③ Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ④ Keep the current as low as possible
  • Purpose ① Stainless steel (308L) • LPG, LNG storage tank
  • Attribute ① Good impact value up to -196°C

    ② Easy to remove slag

    ③ Low spatter

S-308Mo.16

Stainless Steel S-308Mo.16

Type Rutile
Industry Steel Fabrication
JIS Z3221 ES308Mo-16
EN ISO 3581- A - E 20 10 3
KS
AWS A5.4/ASME SFA5.4 E308Mo-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Remove dirts such as oil and dust from the groove.

    ③ Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ④ Keep the current as low as possible
  • Purpose ① Stainless steel (ASTM CF8M)
  • Attribute ① Easy to remove slag

    ② Smooth welding

    ③ Low spatter

S-308L.16N

Stainless Steel S-308L.16N

Type Rutile
Industry Shipbulding|Offshore Structures|Energy & Power Plants|Steel Fabricatio
JIS Z3221 ES308L-16
EN ISO 3581- A - E 19 9 L R
KS D7014 E308L-16
AWS A5.4/ASME SFA5.4 E308L-16
  • Caution ① It is mostly effective to proceed with welding, keeping the arc as short as possible in flat position.

    ② Remove dirts such as oil and dust from the groove.

    ③ Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ④ Keep the current as low as possible
  • Purpose ① Stainless steel (low carbon 18%Cr-8%Ni)
  • Attribute ① Good resistance to corrosion and oxidizing environments

    ② Easy to remove slag

    ③ Good bead appearance

    ④ High moisture resistance (17 type)

S-308.16N

Stainless Steel S-308.16N

Type Rutile
Industry
JIS Z3221 ES308-16
EN ISO 3581- A - E 19 9 R
KS D7014 E308-16
AWS A5.4/ASME SFA5.4 E308-16
  • Caution ① Keep the arc as short as possible.

    ② Remove dirts such as oil and dust from the groove.

    ③ Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ④ Keep the current as low as possible
  • Purpose ① Stainless steel (18%Cr-8%Ni)
  • Attribute ① Good resistance to corrosion and oxidizing environments

    ② Easy to remove slag

    ③ Low spatter

    ④ Good bead appearance

S-307.16

Stainless Steel S-307.16

Type Rutile
Industry
JIS
EN 1600 E 18 8 Mn R 1 2
KS
AWS
  • Caution ① Remove dirts such as oil and dust from the groove.

    ② Dry the electrodes at 350℃(662℉) for 60 minutes before use.

    ③ Keep the arc as short as possible and Keep the current as low as possible
  • Purpose ① Stainless steel(18%Cr-8%), 13% Mn steel, Dissimilar welding
  • Attribute ① Low crack sensitivity in high temperature

    ② Easy to remove slag

    ③ Low spatter

    ④ Good bead appearance